DB32/T—2022
目次
前言.................................................................................VI
1范圍...............................................................................1
2規(guī)范性引用文件.....................................................................1
3術(shù)語和定義.........................................................................2
4符號和縮略語.......................................................................5
5總體要求...........................................................................6
6基層、底基層.......................................................................6
6.1一般規(guī)定.......................................................................6
6.2抗裂嵌擠型水泥穩(wěn)定碎石基層、底基層.............................................6
6.3密級配瀝青碎石混合料基層......................................................12
6.4級配碎石底基層................................................................13
6.5質(zhì)量管理和檢查驗收............................................................15
7下封層、粘層......................................................................18
7.1下封層........................................................................18
7.2粘層..........................................................................19
7.3質(zhì)量管理和檢查驗收............................................................20
8水泥混凝土橋面防水粘結(jié)層..........................................................20
8.1一般規(guī)定......................................................................20
8.2材料要求......................................................................21
8.3施工準(zhǔn)備......................................................................21
8.4施工..........................................................................21
8.5質(zhì)量管理和檢查驗收............................................................22
9面層..............................................................................22
9.1一般規(guī)定......................................................................22
9.2材料要求......................................................................23
9.3瀝青混合料技術(shù)要求............................................................27
9.4瀝青混合料配合比設(shè)計..........................................................29
9.5下承層的檢查與處理............................................................31
9.6機(jī)械與試驗儀器................................................................32
9.7首件工程......................................................................32
9.8施工..........................................................................33
9.9其他瀝青混合料................................................................36
9.10質(zhì)量管理和檢查驗收...........................................................40
10改擴(kuò)建工程.......................................................................42
10.1一般規(guī)定.....................................................................42
10.2材料要求.....................................................................42
I
DB32/T—2022
10.3舊路面的處理..................................................................42
10.4新舊路面鋪筑及拼接............................................................43
11施工信息自動采集與預(yù)警............................................................46
11.1一般規(guī)定......................................................................46
11.2數(shù)據(jù)采集與傳輸................................................................46
11.3數(shù)據(jù)分析與預(yù)警處理............................................................48
附錄A(規(guī)范性)施工機(jī)械............................................................49
附錄B(規(guī)范性)質(zhì)量檢測儀器........................................................52
附錄C(資料性)ATB-25瀝青碎石混合料目標(biāo)配合比設(shè)計實例..............................55
附錄D(規(guī)范性)不粘輪試驗規(guī)程......................................................59
附錄E(規(guī)范性)AC-S瀝青混合料要求..................................................61
附錄F(規(guī)范性)公路瀝青60℃旋轉(zhuǎn)粘度試驗規(guī)程........................................62
附錄G(規(guī)范性)多應(yīng)力蠕變恢復(fù)(MSCR)試驗方法檢測規(guī)程...............................64
附錄H(資料性)玄武巖高溫抗剝落性能試驗規(guī)程.........................................68
附錄I(規(guī)范性)粗集料高溫壓碎值試驗規(guī)程.............................................70
附錄J(規(guī)范性)液體材料滲透性試驗規(guī)程..............................................72
附錄K(資料性)SMA-13S瀝青混合料目標(biāo)配合比設(shè)計實例.................................74
附錄L(資料性)Superpave20瀝青混合料目標(biāo)配合比設(shè)計實例.............................78
附錄M(規(guī)范性)地推式直剪試驗檢測規(guī)程..............................................84
參考文獻(xiàn)..............................................................................85
圖C.1混合料密度及體積指標(biāo)與油石比關(guān)系曲線..........................................57
圖D.1粘輪測試儀示意圖.............................................................59
圖F.1布洛克菲爾德粘度計示意圖......................................................62
圖G.1動態(tài)剪切流變儀基本原理示意圖..................................................64
圖K.1級配曲線圖....................................................................75
圖L.1設(shè)計級配曲線..................................................................80
圖M.1地推式直剪試驗裝置示意圖......................................................84
表1水泥質(zhì)量要求.....................................................................7
表2集料備料規(guī)格.....................................................................7
表3粗集料技術(shù)要求...................................................................7
表4細(xì)集料技術(shù)要求...................................................................7
表5抗裂嵌擠型(低劑量)水泥穩(wěn)定碎石混合料級配范圍....................................9
表6密級配瀝青碎石混合料級配范圍....................................................12
表7密級配瀝青碎石混合料大馬歇爾試驗設(shè)計要求.........................................12
表8級配碎石底基層用集料質(zhì)量技術(shù)要求................................................13
表9級配碎石級配組成范圍............................................................13
II
DB32/T—2022
表10水泥、集料的質(zhì)量標(biāo)準(zhǔn)...........................................................15
表11抗裂嵌擠型水泥穩(wěn)定碎石基層、底基層質(zhì)量控制標(biāo)準(zhǔn).................................16
表12級配碎石底基層施工過程中質(zhì)量檢查標(biāo)準(zhǔn)...........................................17
表13SBS改性乳化瀝青技術(shù)要求.......................................................18
表14集料級配范圍...................................................................19
表15不粘輪乳化瀝青技術(shù)要求.........................................................20
表16下封層質(zhì)量檢查項目及質(zhì)量標(biāo)準(zhǔn)...................................................20
表17水泥混凝土橋面防水粘結(jié)層的檢驗標(biāo)準(zhǔn).............................................22
表1870號道路石油瀝青技術(shù)要求......................................................23
表19SBS改性瀝青技術(shù)要求...........................................................23
表20面層用粗集料技術(shù)要求...........................................................24
表21粗集料供料品種控制篩孔尺寸.....................................................25
表22面層用細(xì)集料規(guī)格...............................................................25
表23面層用細(xì)集料技術(shù)要求...........................................................25
表24面層用礦粉的技術(shù)要求...........................................................26
表25抗剝落劑技術(shù)要求...............................................................26
表26封水劑技術(shù)要求.................................................................27
表27SMA-13S瀝青混合料馬歇爾試驗設(shè)計技術(shù)要求.......................................27
表28SMA-13S瀝青混合料配合比檢驗技術(shù)要求...........................................27
表29Superpave20瀝青混合料配合比設(shè)計及驗證試驗技術(shù)要求.............................28
表30Superpave25瀝青混合料配合比設(shè)計及驗證試驗技術(shù)要求.............................28
表31SMA-13S瀝青混合料級配范圍.....................................................29
表32Superpave瀝青混合料級配控制點和限制區(qū)界限.....................................29
表33瀝青混合料施工溫度.............................................................33
表34Superpave混合料碾壓速度.......................................................34
表35SMA-13S混合料碾壓速度.........................................................35
表36高模量劑質(zhì)量技術(shù)要求...........................................................36
表37HMM級配范圍...................................................................36
表38HMM配合比設(shè)計檢驗技術(shù)要求.....................................................36
表39HMM的施工溫度.................................................................37
表40建議施工碾壓方案...............................................................38
表41巖瀝青質(zhì)量技術(shù)要求.............................................................38
表42RAC-20級配范圍................................................................38
表43RAC-20馬歇爾試驗設(shè)計及檢驗要求................................................38
表44RAC-20的施工溫度..............................................................40
表45建議施工碾壓方案...............................................................40
表46瀝青路面各面層施工階段的質(zhì)量檢查標(biāo)準(zhǔn)...........................................40
表47界面劑技術(shù)要求.................................................................44
表48基層、底基層拼接縫施工質(zhì)量控制要求.............................................44
表49面層拼接縫施工質(zhì)量控制要求.....................................................45
表50改性瀝青生產(chǎn)指標(biāo)及采集頻率.....................................................46
表51瀝青運輸指標(biāo)及采集頻率.........................................................46
表52瀝青試驗檢測指標(biāo)及采集頻率.....................................................46
III
DB32/T—2022
表53瀝青混合料拌和生產(chǎn)指標(biāo)及采集頻率................................................47
表54瀝青混合料運輸指標(biāo)及采集頻率...................................................47
表55瀝青混合料攤鋪指標(biāo)及采集頻率...................................................47
表56瀝青混合料壓實指標(biāo)及采集頻率...................................................48
表A.1底基層、基層施工機(jī)械設(shè)備配置..................................................49
表A.2SMA-13S上面層施工機(jī)械設(shè)備配置.................................................49
表A.3Superpave面層施工機(jī)械設(shè)備配置.................................................50
表A.4HMM面層施工機(jī)械設(shè)備配置.......................................................50
表A.5RAC面層施工機(jī)械設(shè)備配置.......................................................50
表A.6下封層施工機(jī)械設(shè)備配置........................................................51
表A.7橋面防水粘結(jié)層施工機(jī)械設(shè)備配置................................................51
表B.1基層、底基層質(zhì)量檢測儀器配置..................................................52
表B.2瀝青面層質(zhì)量檢測儀器配置......................................................52
表B.3下封層質(zhì)量檢測儀器配置........................................................53
表B.4橋面防水粘結(jié)層質(zhì)量檢測儀器配置................................................54
表C.1各種集料篩分結(jié)果.............................................................55
表C.2各級配各種集料組成...........................................................55
表C.3混合料級配表.................................................................55
表C.4各級配的大馬歇爾試驗結(jié)果.....................................................55
表C.5各級配混合料SSC試驗結(jié)果.....................................................56
表C.6設(shè)計級配不同油石比時大馬歇爾試驗結(jié)果..........................................57
表C.7設(shè)計級配各項指標(biāo).............................................................57
表C.8水穩(wěn)定性試驗結(jié)果.............................................................58
表C.9動穩(wěn)定度試驗結(jié)果.............................................................58
表C.10無側(cè)限抗壓強(qiáng)度試驗結(jié)果(20℃)..............................................58
表E.1AC-20S、AC-25S瀝青混合料級配組成.............................................61
表G.1控制和數(shù)據(jù)采集系統(tǒng)精度要求...................................................64
表H.1瀝青混合料試樣數(shù)量...........................................................68
表H.2瀝青混合料試樣數(shù)量...........................................................68
表K.1各種集料的篩分結(jié)果...........................................................74
表K.2集料密度試驗結(jié)果.............................................................74
表K.3SMA-13S瀝青混合料三種級配的設(shè)計組成結(jié)果......................................74
表K.4VCADRC測試結(jié)果.................................................................75
表K.5初試級配的體積分析...........................................................75
表K.6馬歇爾試驗結(jié)果...............................................................75
表K.7析漏試驗結(jié)果.................................................................76
表K.8飛散試驗結(jié)果.................................................................76
表K.9浸水馬歇爾試驗結(jié)果...........................................................76
表K.10車轍試驗動穩(wěn)定度............................................................76
表K.11小梁彎曲試驗結(jié)果............................................................77
表K.12級配及最佳油石比............................................................77
表L.1集料相對密度試驗結(jié)果表.......................................................78
表L.2集料篩分結(jié)果表...............................................................78
IV
DB32/T—2022
表L.3級配組成表...................................................................78
表L.4三種試驗級配旋轉(zhuǎn)壓實試驗結(jié)果匯總表...........................................79
表L.5三種級配估算瀝青用量試驗結(jié)果評價表...........................................79
表L.6設(shè)計級配四種瀝青用量試驗結(jié)果匯總表...........................................80
表L.7四種瀝青用量瀝青混合料體積性質(zhì)...............................................81
表L.8設(shè)計瀝青用量驗證試驗結(jié)果表...................................................81
表L.9瀝青混合料體積性質(zhì)表.........................................................81
表L.10瀝青混合料馬歇爾試驗結(jié)果....................................................82
表L.11車轍試驗動穩(wěn)定度試驗結(jié)果....................................................82
表L.12浸水馬歇爾穩(wěn)定度試驗結(jié)果....................................................82
表L.13凍融劈裂試驗結(jié)果............................................................82
表L.14小梁彎曲試驗結(jié)果............................................................83
表L.15級配及設(shè)計油石比............................................................83
V
DB32/T—2022
前言
本文件按照GB/T1.1—2020《標(biāo)準(zhǔn)化工作導(dǎo)則第1部分:標(biāo)準(zhǔn)化文件的結(jié)構(gòu)和起草規(guī)則》的規(guī)定
起草。
本文件代替DB32/T1087—2008《江蘇省高速公路瀝青路面施工技術(shù)規(guī)范》,與DB32/T1087—2008
相比除了編輯性修改外,主要技術(shù)變化如下:
a)更改了部分術(shù)語(見第3章,2008年版的第3章);
b)更改了部分符號(見第4章,2008年版的第4章);
c)更改了底基層、基層(見第6章,2008年版的第6章、第7章);
d)刪除了石灰粉煤灰穩(wěn)定土底基層(見2008年版的6.2);
e)更改了抗裂嵌擠型水泥穩(wěn)定碎石基層、底基層(見6.2,2008年版的6.4、7.2);
f)刪除了石灰粉煤灰碎石基層、底基層(見2008年版的6.4、7.3);
g)刪除了路面透層(見2008年版的8.1);
h)更改了路面下封層、粘層技術(shù)要求(見7.1、7.2,2008年版的8.2、8.3);
i)更改了水泥混凝土橋面防水粘結(jié)層(見第8章,2008年版的第9章)
j)更改了面層材料、瀝青混合料技術(shù)要求(見9.2、9.3,2008年版的10.2、10.3);
k)刪除了面層中AC/AK瀝青混合料相關(guān)要求(見2008年版的第10章);
l)增加了高模量瀝青混合料、巖瀝青混合料技術(shù)要求(見9.9);
m)更改了新舊路面基層、面層拼接方法(見10.3、10.4,2008年版的11.3、11.4);
n)增加了施工信息自動采集與預(yù)警(見第11章);
o)更改了“施工機(jī)械”、“質(zhì)量檢測儀器”、“熱拌瀝青混合料馬歇爾試驗設(shè)計方法”、“瀝
青混合料Superpave配合比設(shè)計方法”、“ATB瀝青碎石混合料的配合比設(shè)計”(見附錄A、
附錄B、附錄K、附錄L、附錄C,2008年版的附錄A、附錄B、附錄C、附錄D);
p)刪除了“施工質(zhì)量動態(tài)管理方法”(見2008年版附錄E);
q)增加了“不粘輪試驗規(guī)程”、“AC-S瀝青混合料要求”、“公路瀝青60℃旋轉(zhuǎn)粘度試驗規(guī)程”、
“多應(yīng)力蠕變恢復(fù)(MSCR)試驗方法檢測規(guī)程”、“玄武巖高溫抗剝落性能試驗規(guī)程”、“粗
集料高溫壓碎值試驗規(guī)程”、“液體材料滲透性試驗規(guī)程”、“地推式直剪試驗檢測規(guī)程”
(見附錄D、附錄E、附錄F、附錄G、附錄H、附錄I、附錄J、附錄M)。
請注意本文件的某些內(nèi)容可能涉及專利。本文件的發(fā)布機(jī)構(gòu)不承擔(dān)識別專利的責(zé)任。
本文件由江蘇省交通運輸廳提出并歸口。
本文件起草單位:江蘇省交通工程建設(shè)局、江蘇中路工程技術(shù)研究院有限公司、中路交科科技股份
有限公司。
本文件主要起草人:蔣振雄、劉世同、潘衛(wèi)育、張志祥、杜騁、金光來、劉朝暉、邵學(xué)富、陸宇、
李一鶴、楊光昊、張孝勝、王祥波、蔡文龍、臧國帥、劉海婷、曹陽、張志超、余雪娟、吳德磊、王兆
鑫、陳兆南、馬仕亮、王罡。
本文件及其所代替文件的歷次版本發(fā)布情況為:
——2008年首次發(fā)布為DB32/T1087—2008;
——本次為第一次修訂。
VI
DB32/T—2022
高速公路瀝青路面施工技術(shù)規(guī)范
1范圍
本文件規(guī)定了高速公路瀝青路面底基層、基層、下封層、粘層、水泥混凝土橋面防水粘結(jié)層、面層
等施工技術(shù)要求,改擴(kuò)建工程、施工信息自動采集與預(yù)警等要求。
本文件適用于高速公路新建、改擴(kuò)建瀝青路面等工程,其他等級公路可參照執(zhí)行。
2規(guī)范性引用文件
下列文件中的內(nèi)容通過文中的規(guī)范性引用而構(gòu)成本文件必不可少的條款。其中,注日期的引用文件,
僅該日期對應(yīng)的版本適用于本文件;不注日期的引用文件,其最新版本(包括所有的修改單)適用于本
文件。
GB/T1346水泥標(biāo)準(zhǔn)稠度用水量、凝結(jié)時間、安定性檢驗方法
GB/T3682.1塑料熱塑性塑料熔體質(zhì)量流動速率(MFR)和熔體體積流動速率(MVR)的測定第1
部分:標(biāo)準(zhǔn)方法
GB/T5210色漆和清漆拉開法附著力試驗
GB/T17671水泥膠砂強(qiáng)度檢驗方法(ISO法)
GB/T19466.3塑料差示掃描量熱法(DSC)第3部分:熔融和結(jié)晶溫度及熱焓的測定
JCT975道橋用防水涂料
JGJ63混凝土用水標(biāo)準(zhǔn)
JT/T533瀝青路面用纖維
JT/T798路用廢胎膠粉橡膠瀝青
JTG3430公路土工試驗規(guī)程
JTG3450公路路基路面現(xiàn)場測試規(guī)程
JTG5142公路瀝青路面養(yǎng)護(hù)技術(shù)規(guī)范
JTG5421公路瀝青路面養(yǎng)護(hù)設(shè)計規(guī)范
JTG/T5521公路瀝青路面再生技術(shù)規(guī)范
JTGD50公路瀝青路面設(shè)計規(guī)范
JTGE20公路工程瀝青及瀝青混合料試驗規(guī)程
JTGE30公路工程水泥及水泥混凝土試驗規(guī)程
JTGE41公路工程巖石試驗規(guī)程
JTGE42公路工程集料試驗規(guī)程
JTGE51公路工程無機(jī)結(jié)合料穩(wěn)定材料試驗規(guī)程
JTG/TF20公路路面基層施工技術(shù)細(xì)則
JTGF40公路瀝青路面施工技術(shù)規(guī)范
JTGF80/1公路工程質(zhì)量檢驗評定標(biāo)準(zhǔn)第一冊土建工程
DB32/T2285水泥混凝土橋面水性環(huán)氧瀝青防水粘結(jié)層施工技術(shù)規(guī)范
DB32/T3821公路養(yǎng)護(hù)工程排水瀝青路面技術(shù)規(guī)范
DB32/TXXXX瀝青紅外光譜指紋識別與SBS摻量試驗檢測規(guī)程
1
DB32/T—2022
3術(shù)語和定義
下列術(shù)語和定義適用于本文件。
3.1
基層base
直接位于瀝青路面面層下的主要承重層。
[來源:JTG/TF20—2015,2.0.1,有修改]
3.2
底基層subbase
在瀝青路面基層下鋪裝的次要承重層。
[來源:JTG/TF20—2015,2.0.2,有修改]
3.3
抗裂嵌擠型水泥穩(wěn)定碎石cementstabilizedmaterialwithcrackresistanceandinterlock
characteristics
通過混合料合成級配的控制,形成骨架嵌擠結(jié)構(gòu)的水泥穩(wěn)定碎石混合料。
[來源:DB32/T3311—2017,3.3]
3.4
抗裂嵌擠型低劑量水泥穩(wěn)定碎石low-dosecementstabilizedmaterialwithcrackresistance
andinterlockcharacteristics
采用較低劑量(一般小于3%)的水泥,通過混合料合成級配的控制,形成骨架嵌擠結(jié)構(gòu)的水泥穩(wěn)
定碎石混合料。
3.5
級配碎石gradedcrushedstone
各檔粒徑的碎石和石屑按一定比例混合,級配滿足一定要求且塑性指數(shù)和承載比均符合規(guī)定要求的
混合料。
[來源:JTG/TF20—2015,2.0.7]
3.6
松鋪系數(shù)coefficientofloosepavingmaterial
材料的松鋪厚度與達(dá)到規(guī)定壓實度的壓實厚度之比值。
[來源:JTG/TF20—2015,2.0.10]
3.7
集料aggregate
在混合料中起骨架和填充作用的粒料,包括碎石、石屑、砂等。
[來源:JTGE42—2005,2.1.1]
3.8
填料filler
在瀝青混合料中起填充作用的粒徑小于0.075mm的礦物質(zhì)粉末。通常是石灰石等堿性石料加工磨細(xì)
得到的礦粉,水泥、消石灰、粉煤灰等礦物質(zhì)有時也可作為填料使用。
[來源:JTGE42—2005,2.1.9]
3.9
聚合物纖維polymerfiber
2
DB32/T—2022
以合成高分子聚合物為原料制成的化學(xué)纖維。
[來源:JT/T533—2020,3.3]
3.10
集料最大粒徑maximumsizeofaggregate
指集料的100%都要求通過的最小的標(biāo)準(zhǔn)篩篩孔尺寸。
[來源:JTGE42—2005,2.1.27]
3.11
集料的公稱最大粒徑nominalmaximumsizeofaggregate
指集料有少量不通過(一般容許篩余不超過10%)的最小標(biāo)準(zhǔn)篩篩孔尺寸。通常比集料最大粒徑小
一個粒級。
[來源:JTGE42—2005,2.1.28]
3.12
瀝青結(jié)合料Asphaltbinder,Asphaltcement
在瀝青混合料中起膠結(jié)作用的瀝青類材料(含添加的外摻劑、改性劑等)的總稱。
[來源:JTGF40—2004,2.1.1]
3.13
乳化瀝青emulsifiedbitumen(英),asphaltemulsion,emulsifiedasphalt(美)
石油瀝青(或煤瀝青)與水在乳化劑、穩(wěn)定劑的作用下經(jīng)乳化加工制得的均勻的瀝青產(chǎn)品,也稱瀝
青乳液。
[來源:JTGF40—2004,2.1.2]
3.14
改性瀝青modifiedbitumen(英),modifiedasphalt(美)
摻加橡膠、樹脂、高分子聚合物、天然瀝青、磨細(xì)的橡膠粉或者其他材料等外摻劑(改性劑)制成
的瀝青結(jié)合料,從而使瀝青或瀝青混合料的性能得以改善。
[來源:JTGF40—2004,2.1.4]
3.15
改性乳化瀝青modifiedemulsifiedbitumen(英),modifiedasphaltemulsion(美)
在制作乳化瀝青的過程中同時加入聚合物膠乳,或?qū)⒕酆衔锬z乳與乳化瀝青成品混合,或?qū)酆衔?/p>
改性瀝青進(jìn)行乳化加工得到的乳化瀝青產(chǎn)品。
[來源:JTGF40—2004,2.1.5]
3.16
不粘輪乳化瀝青non-stickwheelemulsifiedasphalt
由特種瀝青與乳化劑、改性劑、穩(wěn)定劑等制備而成的,具有較強(qiáng)粘結(jié)性能及抵抗施工機(jī)械輪胎、履
帶等損傷性能的粘層材料。
3.17
粘(黏)層tackcoat
路面結(jié)構(gòu)中起粘結(jié)作用的功能層。
[來源:JTGD50—2017,2.1.9]
3.18
封層sealcoat
路面結(jié)構(gòu)中用以阻止水下滲的功能層。
3
DB32/T—2022
[來源:JTGD50—2017,2.1.8]
3.19
橋面防水粘結(jié)層bridgedeckwaterproofbondinglayer
設(shè)在橋面水泥混凝土鋪裝層與瀝青鋪裝層之間,起防水和粘結(jié)作用的薄層。
3.20
傅立葉變換紅外光譜fouriertransforminfraredspectroscopy
FTIR
一種通過獲得固體,液體或氣體的紅外線吸收光譜和放射光譜。
注:可用于評價瀝青相似度與測定改性瀝青中SBS含量。
3.21
瀝青旋轉(zhuǎn)粘度asphaltrotationalviscosity
采用布洛克菲爾德粘度計測定瀝青試樣流動時形成的抵抗力或內(nèi)部阻力度量。
3.22
多應(yīng)力蠕變恢復(fù)multiplestresscreeprecovery
MSCR
瀝青試樣經(jīng)過不同應(yīng)力水平下力的一定周期作用后,瀝青的應(yīng)變恢復(fù)率。
3.23
封水劑sealingagent
用于封堵瀝青路面表面空隙及微裂縫,以提高瀝青路面密水性的材料。
3.24
瀝青混合料bituminousmixtures(英),asphaltmixtures(美)
由礦料與瀝青結(jié)合料拌和而成的混合料的總稱。按材料組成及結(jié)構(gòu)分為連續(xù)級配、間斷級配混合料。
按礦料級配組成及空隙率大小分為密級配、半開級配、開級配混合料。按公稱最大粒徑的大小可分為特
粗式(公稱最大粒徑等于或大于31.5mm)、粗粒式(公稱最大粒徑26.5mm)、中粒式(公稱最大粒徑16mm
或19mm)、細(xì)粒式(公稱最大粒徑9.5mm或13.2mm)、砂粒式(公稱最大粒徑小于9.5mm)瀝青混合料。
[來源:JTGF40—2004,2.1.12]
3.25
瀝青瑪蹄脂碎石混合料stonemasticasphalt(英),stonematrixasphalt(美)
由瀝青膠結(jié)料與少量的纖維穩(wěn)定劑、細(xì)集料以及較多量的填料(礦粉)組成的瀝青瑪蹄脂,填充于
間斷級配的粗集料骨架間隙,組成一體形成的瀝青混合料,簡稱SMA。
[來源:JTGF40—2004,2.1.18]
3.26
密級配瀝青碎石混合料(瀝青穩(wěn)定碎石基層)dense-gradedasphaltgravelmixture(asphalt
treatedbase)
ATB
由礦料和瀝青組成的有一定級配要求的密級配瀝青處治碎石混合料。
3.27
高模量瀝青混合料highmodulusmixture
HMM
采用硬質(zhì)瀝青、硬質(zhì)瀝青顆?;蚋吣A縿┑茸鳛樘砑觿┡c瀝青、集料拌和成型,具有設(shè)計空隙率小、
高模量、抗車轍、密水等特點,用于路面抗車轍層的混合料。
4
DB32/T—2022
3.28
巖瀝青混合料rockasphaltmixture
RAC
采用天然巖瀝青作為添加劑與瀝青、集料拌和成型,具有抗車轍性能好、強(qiáng)度高等特點,用于路面
抗車轍層的混合料。
4符號和縮略語
下列符號適用于本文件。
C:集料的瀝青吸收系數(shù)
Pa:瀝青混合料的油石比
Pb:瀝青混合料中的瀝青用量
Pbe:瀝青混合料中的有效瀝青用量
γb:瀝青的相對密度
γsa:瀝青混合料中合成礦料的表觀相對密度
γsb:瀝青混合料中合成礦料的毛體積相對密度
γse:瀝青混合料中合成礦料的有效相對密度
γt:瀝青混合料的最大理論相對密度
下列縮略語適用于本文件。
AC-S:適用于江蘇省高速公路的密級配瀝青混合料
ATB:密級配瀝青碎石混合料
CBR:加州承載比
DP:瀝青混合料的粉膠比(0.075mm通過率與有效瀝青含量的比值)
DS:動穩(wěn)定度
FL:馬歇爾試驗的流值
FTIR:傅立葉變換紅外光譜
HMM:高模量瀝青混合料
MS:馬歇爾穩(wěn)定度
MSCR:多應(yīng)力蠕變恢復(fù)
OAC:最佳瀝青用量
OGFC:開級配抗滑表層
PG:美國瀝青膠結(jié)料路用性能分級規(guī)范
PI:瀝青膠結(jié)料針入度指數(shù)
RAC:巖瀝青混合料
RTFOT/TFOT:旋轉(zhuǎn)薄膜加熱(薄膜加熱)試驗
SBS:苯乙烯—丁二烯—苯乙烯嵌段共聚物
SGC:旋轉(zhuǎn)壓實試驗機(jī)
SMA-S:適用于江蘇省高速公路的瀝青瑪蹄脂碎石混合料
SuperpaveTM:美國公路戰(zhàn)略研究計劃
TSR:凍融劈裂試驗強(qiáng)度比
5
DB32/T—2022
VCA:粗集料骨架間隙率
VCADRC:搗實狀態(tài)下的粗集料松裝間隙率
VCAmix:壓實瀝青混合料的粗集料骨架間隙率
VFA:壓實瀝青混合料中的瀝青飽和度
VMA:壓實瀝青混合料的礦料間隙率
VV:壓實瀝青混合料的空隙率
5總體要求
5.1應(yīng)結(jié)合本地實際選擇高速公路瀝青路面合適的結(jié)構(gòu)和材料,鼓勵采用經(jīng)試驗和實踐檢驗的新技術(shù)、
新材料、新設(shè)備、新工藝。
5.2應(yīng)執(zhí)行國家環(huán)境和生態(tài)保護(hù)、安全生產(chǎn)的相關(guān)規(guī)定。
5.3應(yīng)編制施工組織設(shè)計方案。
5.4試驗檢測的試驗室和試驗人員應(yīng)取得相應(yīng)的資質(zhì),儀器設(shè)備應(yīng)檢定合格。
6基層、底基層
6.1一般規(guī)定
6.1.1高速公路瀝青路面基層宜采用抗裂嵌擠型水泥穩(wěn)定碎石。
6.1.2根據(jù)工程實際情況和各類基層的適用條件,可選擇其他的基層類型,如密級配瀝青碎石基層、
開級配瀝青碎石基層等。
6.1.3可采用雙層連鋪或整層一次性全厚度攤鋪施工。
注1:雙層連鋪是指在施工完下基層適當(dāng)長度后,即刻施工上基層的一種施工方式。
注2:整層一次性全厚度攤鋪是指采用大功率攤鋪機(jī)一次性攤鋪兩層基層,并碾壓成型至基層設(shè)計厚度的一種施工
方式。
6.1.4高速公路瀝青路面底基層宜采用抗裂嵌擠型低劑量水泥穩(wěn)定碎石,可采用廠拌水泥再生碎石、
級配碎石等。
6.1.5廠拌水泥再生碎石底基層,應(yīng)按照J(rèn)TG/T5521的有關(guān)規(guī)定執(zhí)行。
6.1.6應(yīng)控制基層、底基層厚度和高程,其橫坡應(yīng)與面層一致?;鶎?、底基層表面高出設(shè)計標(biāo)高部分
應(yīng)銑刨處理;局部標(biāo)高低于驗收標(biāo)準(zhǔn),應(yīng)銑刨重鋪。
6.2抗裂嵌擠型水泥穩(wěn)定碎石基層、底基層
6.2.1一般要求
6.2.1.1高速公路瀝青路面基層、底基層采用抗裂嵌擠型水泥穩(wěn)定碎石結(jié)構(gòu)時,應(yīng)采用集中廠拌工藝,
單層壓實厚度宜為18cm~20cm。
6.2.1.2抗裂嵌擠型水泥穩(wěn)定碎石混合料采用干質(zhì)量配合比計算,以集料100,水泥劑量外加的外比
表示。
6.2.1.3宜在氣溫較高的季節(jié)組織施工。施工期的日最低氣溫應(yīng)在5℃以上,在有冰凍的地區(qū),應(yīng)在
第一次重冰凍到來的15d~30d之前完成施工。
注:重冰凍的標(biāo)準(zhǔn)一般指氣溫達(dá)到-3℃~-5℃。
6
DB32/T—2022
6.2.1.4應(yīng)盡可能縮短從加水拌和到碾壓終了的延遲時間,延遲時間不應(yīng)超過水泥的初凝時間。
6.2.1.5雨季施工時,應(yīng)避免抗裂嵌擠型水泥穩(wěn)定碎石混合料遭雨淋。
6.2.1.6應(yīng)采取有效措施,防止抗裂嵌擠型水泥穩(wěn)定碎石基層、底基層在施工中出現(xiàn)離析和開裂現(xiàn)象,
對已經(jīng)出現(xiàn)的離析和開裂應(yīng)進(jìn)行處理。
6.2.2材料要求
6.2.2.1水泥
6.2.2.1.1普通硅酸鹽水泥、礦渣硅酸鹽水泥、火山灰質(zhì)硅酸鹽水泥都可用于拌和抗裂嵌擠型水泥穩(wěn)
定碎石混合料,宜采用強(qiáng)度等級不低于42.5級的緩凝水泥,水泥初凝、終凝時間應(yīng)符合表1規(guī)定,其
他指標(biāo)應(yīng)符合JTGE30與GB/T1346的規(guī)定。
6.2.2.1.2采用散裝水泥,安定性應(yīng)檢測合格后入罐使用,水泥溫度應(yīng)不高于50℃。
表1水泥質(zhì)量要求
項次檢測項目技術(shù)要求試驗方法
1初凝時間>3h
GB/T1346
2終凝時間>6h且<10h
6.2.2.2集料
6.2.2.2.1集料的最大粒徑為31.5mm,4.75mm及以上為粗集料、4.75mm以下為細(xì)集料。宜按四種及
以上規(guī)格備料,備料規(guī)格應(yīng)符合表2的規(guī)定。
表2集料備料規(guī)格
項次粒徑規(guī)格/mm
1四檔集料13.2~31.54.75~13.22.36~4.750~2.36—
2五檔集料19.0~31.59.5~19.04.75~9.52.36~4.750~2.36
6.2.2.2.2粗集料的技術(shù)要求應(yīng)符合表3的規(guī)定,細(xì)集料的技術(shù)要求應(yīng)符合表4的規(guī)定;粗、細(xì)集料
規(guī)格應(yīng)符合JTG/TF20相關(guān)規(guī)定。
表3粗集料技術(shù)要求
技術(shù)要求
項次檢驗項目試驗方法
基層底基層
1壓碎值≤26%≤30%JTGE42,T0316
2針片狀顆粒含量≤15%JTGE42,T0312
3軟石含量≤5%JTGE42,T0320
4小于0.075mm顆粒含量≤2%JTGE42,T0310
表4細(xì)集料技術(shù)要求
項次檢驗項目技術(shù)要求試驗方法
1液限<28%JTG3430,T0118
2塑性指數(shù)<9JTG3430,T0118
7
DB32/T—2022
表4(續(xù))
項次檢驗項目技術(shù)要求試驗方法
3硫酸鹽含量≤0.25%JTGE42,T0341
4有機(jī)質(zhì)含量<2%JTGE42,T0336
5小于1.18mm顆粒含量(2.36mm~4.75mm規(guī)格)≤5%JTGE42,T0333
6小于0.075mm顆粒含量(0~2.36mm規(guī)格)≤15%JTGE42,T0333
7顆粒分析符合JTG/TF20細(xì)集料規(guī)格要求JTGE42,T0327
6.2.2.3水
飲用水可直接作為拌和與養(yǎng)生用水。非飲用水技術(shù)要求應(yīng)符合JGJ63的規(guī)定。
6.2.3機(jī)械與試驗儀器
應(yīng)配備齊全的施工機(jī)械和試驗儀器,開工前應(yīng)進(jìn)行保養(yǎng)和試機(jī)工作,主要施工機(jī)械和試驗儀器配備
應(yīng)符合附錄A和附錄B要求。
6.2.4配合比設(shè)計
6.2.4.1一般規(guī)定
6.2.4.1.1抗裂嵌擠型水泥穩(wěn)定碎石混合料配合比設(shè)計,分為目標(biāo)配合比設(shè)計與生產(chǎn)配合比設(shè)計。
6.2.4.1.2根據(jù)規(guī)定的材料指標(biāo)要求,通過試驗選取合適的集料和水泥;確定合理的集料配合比例、
最佳水泥劑量、混合料的最佳含水量和相應(yīng)的最大干密度。
6.2.4.1.3為減少基層裂縫,應(yīng)做到三個限制:在滿足設(shè)計強(qiáng)度的基礎(chǔ)上限制水泥用量;同時限制細(xì)
集料用量;根據(jù)施工時氣候條件限制含水量。施工中水泥劑量宜不大于4.2%,合成集料級配中0.075mm
以下顆粒含量宜不大于
溫馨提示
- 1. 本站所有資源如無特殊說明,都需要本地電腦安裝OFFICE2007和PDF閱讀器。圖紙軟件為CAD,CAXA,PROE,UG,SolidWorks等.壓縮文件請下載最新的WinRAR軟件解壓。
- 2. 本站的文檔不包含任何第三方提供的附件圖紙等,如果需要附件,請聯(lián)系上傳者。文件的所有權(quán)益歸上傳用戶所有。
- 3. 本站RAR壓縮包中若帶圖紙,網(wǎng)頁內(nèi)容里面會有圖紙預(yù)覽,若沒有圖紙預(yù)覽就沒有圖紙。
- 4. 未經(jīng)權(quán)益所有人同意不得將文件中的內(nèi)容挪作商業(yè)或盈利用途。
- 5. 人人文庫網(wǎng)僅提供信息存儲空間,僅對用戶上傳內(nèi)容的表現(xiàn)方式做保護(hù)處理,對用戶上傳分享的文檔內(nèi)容本身不做任何修改或編輯,并不能對任何下載內(nèi)容負(fù)責(zé)。
- 6. 下載文件中如有侵權(quán)或不適當(dāng)內(nèi)容,請與我們聯(lián)系,我們立即糾正。
- 7. 本站不保證下載資源的準(zhǔn)確性、安全性和完整性, 同時也不承擔(dān)用戶因使用這些下載資源對自己和他人造成任何形式的傷害或損失。
最新文檔
- 老物業(yè)轉(zhuǎn)讓合同范例
- 耕地用地合同范例
- 青海民族大學(xué)《計算機(jī)與程序設(shè)計基礎(chǔ)》2023-2024學(xué)年第一學(xué)期期末試卷
- 青海警官職業(yè)學(xué)院《就業(yè)指導(dǎo)與創(chuàng)業(yè)教育》2023-2024學(xué)年第一學(xué)期期末試卷
- 青海農(nóng)牧科技職業(yè)學(xué)院《液壓傳動》2023-2024學(xué)年第一學(xué)期期末試卷
- 2024至2030年中國酸奶乳化穩(wěn)定劑行業(yè)投資前景及策略咨詢研究報告
- 2024至2030年中國營養(yǎng)清爽洗發(fā)露行業(yè)投資前景及策略咨詢研究報告
- 甲硝西泮行業(yè)深度研究報告
- 2024至2030年中國消防專用砍刀行業(yè)投資前景及策略咨詢研究報告
- 2024年不銹鋼茶池項目可行性研究報告
- DB12T 1344-2024 城市軌道交通固定資產(chǎn)分類與編碼地方標(biāo)準(zhǔn)
- 人教版(2024)七年級地理上冊5.1《人口與人種》精美課件
- 企業(yè)綠色供應(yīng)鏈建設(shè)實施方案
- 運動治療技術(shù)智慧樹知到答案2024年白城醫(yī)學(xué)高等??茖W(xué)校
- 新蘇教版三年級上冊科學(xué)全冊知識點
- 智能交通系統(tǒng)智慧樹知到答案2024年山東大學(xué)
- 2024年農(nóng)藝工:農(nóng)作物植保員專業(yè)技術(shù)師知識考試題與答案
- 煤氣退火爐控制系統(tǒng)畢業(yè)設(shè)計說明書
- 2024版專升本宣講課件完整版
- 2025數(shù)學(xué)步步高大一輪復(fù)習(xí)講義人教A版復(fù)習(xí)講義含答案
- 因式分解(分組分解法)練習(xí)100題及答案
評論
0/150
提交評論